Comparative studies of electric conductivity and gas sensitivity have been carried out for two types of tin dioxide films (single- and bilayer ones). The free surface area of the bilayer films was increased intentionally by applying the second layer as a thin nanodis-persed tin dioxide layer with a developed relief. The gas sensitivity of the bilayer films has been shown to exceed by 2 to 4 times that of the single-layer ones at the same thickness. This and others features of the bilayer films have been explained by the improved adsorbing ability thereof and, consequently, by a stronger depletion of free charge carriers in the layer at oxygen adsorption.
Проведены сопоставительные исследования электропроводности и газочувствительности пленок диоксида олова двух типов: 1-слойных и 2-слойных. Площадь свободной поверхности 2-слойных пленок была преднамеренно увеличена за счет нанесения второго слоя в виде тонкого нанодисперсного слоя диоксида олова с сильно развитым рельефом. Показано, что при одинаковой толщине газочувствительность 2-слойных пленок в 2—4 раза выше, чем у 1-слойных. Это и другие отличия 2-слойных пленок объяснены их повышенной адсорбционной способностью и, соответственно, более значительным обеднением слоя свободными зарядоносителями при адсорбции кислорода.
Виконано порівняльні дослідження електропровідності та газочутливості плівок діоксиду олова двох типів: одношарових та двошарових. Площа вільної поверхні двошарових плівок була умисно збільшена шляхом нанесення другого шару у формі тонкого нанодисперсного шару діоксиду олова з сильно розвинутим рельєфом. Показано, що при однаковій товщині газочутливість двошарових плівок у 2-4 рази вище, ніж одношарових. Цю та інші відмінності двошарових плівок пояснено їхньою підвищеною адсорбційною здатністю і, відповідно, більш значним збідненням шару вільними носіями заряду при адсорбції кисню.