Co-precipitation conditions of scheelite tungstates have been studied as well as effect of the alkali-earth metal and anion nature and calcination temperature on the luminescence intensity of the compounds. The scheelite structure of the solid solutions obtained has been confirmed X-ray phase analysis. The excitation conditions, luminescence properties, and light-resistance of the compounds under continuous UV irradiation have been exam -ined. The luminescence intensity of Eu doped calcium tungstate has been found to amount 33 % as compared to that of FL-612 luminophor (Y₂O₃:Eu) while that of Tb doped one, 146% as compared to crystal luminophor Gd₂O₂S:Tb.
Исследованы условия совместного осаждения кальций-лантанид-вольфраматов, влияние природы щелочноземельного металла и анионов, а также температуры прокаливания соединений на интенсивность их люминесценции. Рентгенофазовым анализом подтверждено соответствие полученных твердых растворов структуре шеелита. Исследованы условия их возбуждения, люминесцентные свойства и фотостойкость при непрерывном облучении УФ-светом. Установлено, что интенсивность люминесценции вольфрамата кальция, допированного Eu, составляет 33 % от свечения фотолюминофора ФЛ-612 (Y₂O₃:Eu), а допированного Tb — 146 % от свечения кристаллофосфора Gd₂O₂S:Tb.
Досліджено умови ствосадження Kasb4ih-saHTaHifl-BOSb{paMaTiB, вплив природи лужноземельного MeTasy Ta aHioHiB, a тaкoж TeMnepaTypq пропі^ння сполук Ha інтенсивність їх люмінесценції. Peнтгeнoфaзoвим aMsiooM пiдтвepджeнo відповідність здо-бутах твepдих розчинів CTpyKTypi шеелггу. Досліджено умови їх збудження, люміне-сцентаі влacтивocтi Ta фотостійкість пpи бeзпepepвнoмy oпpoмiнeннi УФ-свгглом. BcTa-новлено, що iнтeнcивнicть люмінесценції вoльфpaмaтy кальцію, дoпoвaнoгo Eu, cклaдaє 33 % від свггіння фoтoлюмiнoфopa ФЛ-612 (Y₂O₃:Eu), a дoпoвaнoгo Tb — 146 % від свггіння кpиcтaлoфocфopa Gd₂O₂S:Tb.