Influence of molibdenium under the hightemperature friction of titatium materials on wear

Abstract

The addition of molybdenum into the titanium material Ті—Cr—TiC significantly changes the composition and properties of nanostructural film, which is generated from the friction on air and under high temperatures. Predominant contents of brittle oxide ТiO₂ (rutile) within the films in the process of friction determines the high wear of materials. There is no titanium oxide TiO₂ within the newly generated film of titanium material containing molybdenum whereas hydroxides and molybdenum oxides prevail in terms of quantity and ensure high protective and lubricate properties of the film as well.

Введение молибдена в титановый материал Ті—Сr—ТіС существенно изменяет состав и свойства наноструктурных пленок, образующихся при трении на воздухе и повышенных температурах. Превалирующее содержание в пленке при трении Ті, Ті—Сr—ТіС хрупкого оксида ТiO₂ (рутил) определяет высокий износ материалов. В образующейся пленке титанового материала, содержащего молибден, оксид титана ТiO₂ отсутствует и в количественном отношении преобладают гидроксиды, оксиды молибдена, которые обеспечивают высокие защитные и смазывающие свойства пленки.

Введення молібдену в титановий матеріал Ті—Сг—ТіС значно змінює склад та властивості наноструктурних плівок, які утворюються при терті на повітрі при підвищених температурах. Домінуючий вміст у плівках при терті Ті, Ті—Сг—ТіС крихкого оксиду TiO₂ (рутіл) визначає високий знос матеріалів. У плівки, яка утворюється у титановому матеріалі, що містить молібден, оксид титану TiO₂ відсутній і переважають гидроксиди та оксиди молібдену, які забезпечують високі захисні та мастильні властивості плівок.