In a composite material reinforced by short random fibers, damage results from different elementary failure mechanisms such as matrix micro-cracking, fiber pull out, failure of fiber/matrix interface, failure of fibers, ...

Delamination in the multidirectional laminates under bending loading is often difficult to characterize because of problems involved by excessive deformations ahead of the crack tip and by non-linearities due to large ...